| Testing |
Property |
Method |
Condition |
Unit |
Value |
|
|
Electrical
|
CTI
|
UL746A
|
|
volt
|
0
|
|
Arc Resistance
|
ASTM D495
|
PCL Code
|
|
6
|
|
HAI
|
UL 746A
|
PCL Code
|
|
1
|
|
HWI
|
UL 746A
|
PCL Code
|
|
3
|
|
HVTR
|
|
PCL Code
|
|
2
|
|
Flammability
|
Flammability
|
UL94
|
1/8"
|
class
|
HB
|
|
Mechanical
|
Elongation at Yield
|
ASTM D638
|
50mm/min
|
%
|
18
|
|
IZOD Impact strength
|
ASTM D256
|
1/4″,23℃
|
kg·cm/cm
|
22
|
|
Tensile Modulus
|
ASTM D638
|
50mm/min
|
kg/㎠
|
500
|
|
Flexural Modulus
|
ASTM D790
|
15 mm/min
|
kg/㎠
|
26000
|
|
Flexural Strength
|
ASTM D790
|
15mm/min
|
kg/㎠
|
800
|
|
Physical
|
Melt Index
|
ASTM D1238
|
220℃/10kg
|
g/10min
|
23
|
|
Mold Shrinkage
|
ASTM D955
|
-
|
%
|
0.3~0.5
|
|
Specific Gravity
|
ASTM D792
|
23℃
|
|
1.05
|
|
Thermal
|
Heat Deflection Temp
|
ASTM D648
|
1/4″,18.5kg/㎠(unannealed)
|
˚C
|
93
|
|
Vicat Softening Temp
|
ASTM D1525
|
1kg
|
˚C
|
103
|
|
|
PETROCHEMICALS